Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.

Record Type:	Electronic resources : Monograph/item
Title/Author:	Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells./
Author:	Panchal, Tarang Kiran.
Published:	Ann Arbor : ProQuest Dissertations & Theses, : 2023,
Description:	72 p.
Notes:	Source: Masters Abstracts International, Volume: 85-01.
Contained By:	Masters Abstracts International85-01.
Subject:	Cadmium telluride. -
Online resource:	https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540038
ISBN:	9798379882129

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
Panchal, Tarang Kiran.

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells. - Ann Arbor : ProQuest Dissertations & Theses, 2023 - 72 p.

Source: Masters Abstracts International, Volume: 85-01.

Thesis (M.Sc.)--Purdue University, 2023.

This item must not be sold to any third party vendors.

The solar cells degrade over time in the field due to various environmental conditions including temperature and humidity. Accelerated lifetime testing was used to test solar cells in a short period of time to obtain reliability and predict the lifetime. Accelerated lifetime testing was done on two 10-WATT ACOPOWER rigid mono crystalline silicon solar panel, 2 3-WATT semi-flexible monocrystalline silicon solar panel and 30 Sunyima Mini Monocrystalline Solar Cell to calculate the acceleration factor, mean reliable life through statistical analysis at certain working conditions. Two Damp heat tests were conducted on the samples to find the degradation and potential defects that occur in the solar cell and that data was used for the statistical analysis. Reliasoft ALTA software was used to statistically analyze the experimental data and to predict the lifetime and to find the probability of failure of the solar cells.Peeling tests were conducted to find the adhesion strength between layers of the untested solar cell samples and accelerated life testing (ALT) tested solar cell samples. Tensile tests were conducted to find out the Young's Modulus, yield stress and yield strain of the peel arm from the peeling test. The data from the tests were used to calculate the energy release rate or the fracture energy. A multivariable Regression analysis was done to develop an analytical equation between the energy release rate (Gc) and Temperature & Humidity.

ISBN: 9798379882129Subjects--Topical Terms:

3763449
Cadmium telluride.

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
LDR:02656nmm a2200409 4500 001 2393967
005 20240414211935.5
006 m o d
007 cr#unu||||||||
008 251215s2023 ||||||||||||||||| ||eng d
020 $a 9798379882129
035 $a (MiAaPQ)AAI30540038
035 $a (MiAaPQ)Purdue22783613
035 $a AAI30540038
040 $a MiAaPQ $c MiAaPQ
100 1 $a Panchal, Tarang Kiran. $3 3763448
245 1 0 $a Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
260 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2023
300 $a 72 p.
500 $a Source: Masters Abstracts International, Volume: 85-01.
500 $a Advisor: Kim, Hansung.
502 $a Thesis (M.Sc.)--Purdue University, 2023.
506 $a This item must not be sold to any third party vendors.
520 $a The solar cells degrade over time in the field due to various environmental conditions including temperature and humidity. Accelerated lifetime testing was used to test solar cells in a short period of time to obtain reliability and predict the lifetime. Accelerated lifetime testing was done on two 10-WATT ACOPOWER rigid mono crystalline silicon solar panel, 2 3-WATT semi-flexible monocrystalline silicon solar panel and 30 Sunyima Mini Monocrystalline Solar Cell to calculate the acceleration factor, mean reliable life through statistical analysis at certain working conditions. Two Damp heat tests were conducted on the samples to find the degradation and potential defects that occur in the solar cell and that data was used for the statistical analysis. Reliasoft ALTA software was used to statistically analyze the experimental data and to predict the lifetime and to find the probability of failure of the solar cells.Peeling tests were conducted to find the adhesion strength between layers of the untested solar cell samples and accelerated life testing (ALT) tested solar cell samples. Tensile tests were conducted to find out the Young's Modulus, yield stress and yield strain of the peel arm from the peeling test. The data from the tests were used to calculate the energy release rate or the fracture energy. A multivariable Regression analysis was done to develop an analytical equation between the energy release rate (Gc) and Temperature & Humidity.
590 $a School code: 0183.
650 4 $a Cadmium telluride. $3 3763449
650 4 $a Thermal cycling. $3 3696616
650 4 $a Humidity. $3 3559498
650 4 $a Failure. $3 3561225
650 4 $a Solar energy. $3 520346
650 4 $a Electricity. $3 524507
650 4 $a Weather. $3 523974
650 4 $a Yield stress. $3 3561163
650 4 $a Electric rates. $3 3560701
650 4 $a Adhesion. $3 818212
650 4 $a Photovoltaic cells. $3 604818
650 4 $a Silicon wafers. $3 3681738
650 4 $a Heat. $3 573595
650 4 $a Adhesives. $3 871837
650 4 $a Ultraviolet radiation. $3 676177
650 4 $a Corrosion. $3 3595443
650 4 $a Alternative energy. $3 3436775
650 4 $a Atmospheric sciences. $3 3168354
650 4 $a Condensed matter physics. $3 3173567
650 4 $a Energy. $3 876794
650 4 $a Industrial engineering. $3 526216
650 4 $a Meteorology. $3 542822
650 4 $a Physics. $3 516296
690 $a 0363
690 $a 0725
690 $a 0611
690 $a 0791
690 $a 0546
690 $a 0629
690 $a 0557
690 $a 0605
710 2 $a Purdue University. $3 1017663
773 0 $t Masters Abstracts International $g 85-01.
790 $a 0183
791 $a M.Sc.
792 $a 2023
793 $a English
856 4 0 $u https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540038