Delamination and Fatigue Analysis of...

Theril, Krishnajith.

FindBook

Google Book

Amazon

博客來

Delamination and Fatigue Analysis of Silicon Solar Cells Using Finite Element Method.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Delamination and Fatigue Analysis of Silicon Solar Cells Using Finite Element Method./
作者:	Theril, Krishnajith.
出版者:	Ann Arbor : ProQuest Dissertations & Theses, : 2023,
面頁冊數:	52 p.
附註:	Source: Masters Abstracts International, Volume: 85-01.
Contained By:	Masters Abstracts International85-01.
標題:	Silicon. -
電子資源:	https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540024
ISBN:	9798379875466

Delamination and Fatigue Analysis of Silicon Solar Cells Using Finite Element Method.
Theril, Krishnajith.

Delamination and Fatigue Analysis of Silicon Solar Cells Using Finite Element Method. - Ann Arbor : ProQuest Dissertations & Theses, 2023 - 52 p.

Source: Masters Abstracts International, Volume: 85-01.

Thesis (M.Sc.)--Purdue University, 2023.

This item must not be sold to any third party vendors.

Fracture of silicon solar cells in photovoltaic (PV) modules are widely reported and a wellknown issue in the PV industry, since it is exposed to adverse climatic conditions and varying temperature loads. A commercial silicon solar cell is mainly composed of four different layers. This thesis investigates delamination failure and thermal fatigue failure due to alternating temperature loads using finite element method (FEM) simulation.The delamination of the encapsulant (EVA) layer and the cell interface was simulated using finite element (FE) simulations in the COMSOL Multiphysics software. The adhesion between the layers were modeled using the cohesive zone model (CZM). The CZM parameters such as normal strength and penalty stiffness were used for the bilinear traction-separation law for the cohesive model in a 90-degree configuration. The critical energy release rate (\uD835\uDC3A\uD835\uDC50) was experimentally calculated as one of the CZM parameters. A uniaxial tensile test of the upper layer of the cell was conducted to determine the material properties of the solar cell layers, and that information was later used for FE simulations. To validate the simulation, we compared the peeling force graph from the experiment and FE simulation, and it was found both graphs showed a maximum peeling force of 120 N.Finite element simulations were also conducted to predict the stress variations in the silicon solar cell layer due to alternating temperatures. An alternating temperature function was developed using triangular waveform equations in the COMSOL Multiphysics software. For this simulation, a 3D model of the cell with a 90-degree peel arm was used, like in the peeling simulation. A maximum stress of 7.31 x 10−3\uD835\uDC41/ \uD835\uDC5A2was observed on the encapsulant (EVA)/cell layer, but no delamination was observed for the given temperature range. In future work, we plan to explore the calculation of fatigue life using thermal simulation to predict the reliability of a solar cell.

ISBN: 9798379875466Subjects--Topical Terms:

669429
Silicon.

Delamination and Fatigue Analysis of Silicon Solar Cells Using Finite Element Method.
LDR:03217nmm a2200421 4500 001 2393966
005 20240414211935.5
006 m o d
007 cr#unu||||||||
008 251215s2023 ||||||||||||||||| ||eng d
020 $a 9798379875466
035 $a (MiAaPQ)AAI30540024
035 $a (MiAaPQ)Purdue22754390
035 $a AAI30540024
040 $a MiAaPQ $c MiAaPQ
100 1 $a Theril, Krishnajith. $3 3763447
245 1 0 $a Delamination and Fatigue Analysis of Silicon Solar Cells Using Finite Element Method.
260 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2023
300 $a 52 p.
500 $a Source: Masters Abstracts International, Volume: 85-01.
500 $a Advisor: Kim, Hansung.
502 $a Thesis (M.Sc.)--Purdue University, 2023.
506 $a This item must not be sold to any third party vendors.
520 $a Fracture of silicon solar cells in photovoltaic (PV) modules are widely reported and a wellknown issue in the PV industry, since it is exposed to adverse climatic conditions and varying temperature loads. A commercial silicon solar cell is mainly composed of four different layers. This thesis investigates delamination failure and thermal fatigue failure due to alternating temperature loads using finite element method (FEM) simulation.The delamination of the encapsulant (EVA) layer and the cell interface was simulated using finite element (FE) simulations in the COMSOL Multiphysics software. The adhesion between the layers were modeled using the cohesive zone model (CZM). The CZM parameters such as normal strength and penalty stiffness were used for the bilinear traction-separation law for the cohesive model in a 90-degree configuration. The critical energy release rate (\uD835\uDC3A\uD835\uDC50) was experimentally calculated as one of the CZM parameters. A uniaxial tensile test of the upper layer of the cell was conducted to determine the material properties of the solar cell layers, and that information was later used for FE simulations. To validate the simulation, we compared the peeling force graph from the experiment and FE simulation, and it was found both graphs showed a maximum peeling force of 120 N.Finite element simulations were also conducted to predict the stress variations in the silicon solar cell layer due to alternating temperatures. An alternating temperature function was developed using triangular waveform equations in the COMSOL Multiphysics software. For this simulation, a 3D model of the cell with a 90-degree peel arm was used, like in the peeling simulation. A maximum stress of 7.31 x 10−3\uD835\uDC41/ \uD835\uDC5A2was observed on the encapsulant (EVA)/cell layer, but no delamination was observed for the given temperature range. In future work, we plan to explore the calculation of fatigue life using thermal simulation to predict the reliability of a solar cell.
590 $a School code: 0183.
650 4 $a Silicon. $3 669429
650 4 $a Load. $3 3562902
650 4 $a Software packages. $3 3683488
650 4 $a Thermal cycling. $3 3696616
650 4 $a Failure. $3 3561225
650 4 $a Polyethylene terephthalate. $3 1636477
650 4 $a Protective coatings. $3 685948
650 4 $a Crack initiation. $3 3564902
650 4 $a Adhesives. $3 871837
650 4 $a Stress analysis. $3 3681390
650 4 $a Climate change. $2 bicssc $3 2079509
650 4 $a Crack propagation. $3 3683840
650 4 $a Propagation. $3 3680519
650 4 $a Alternative energy. $3 3436775
650 4 $a Interfacial bonding. $3 3694336
650 4 $a Photovoltaic cells. $3 604818
650 4 $a Deformation. $2 lcstt $3 3267001
650 4 $a Fracture mechanics. $3 558163
650 4 $a Interfaces. $2 gtt $3 834756
650 4 $a Computer science. $3 523869
650 4 $a Condensed matter physics. $3 3173567
650 4 $a Energy. $3 876794
650 4 $a Industrial engineering. $3 526216
650 4 $a Mechanics. $3 525881
650 4 $a Physics. $3 516296
650 4 $a Polymer chemistry. $3 3173488
690 $a 0404
690 $a 0363
690 $a 0984
690 $a 0611
690 $a 0791
690 $a 0546
690 $a 0346
690 $a 0605
690 $a 0495
710 2 $a Purdue University. $3 1017663
773 0 $t Masters Abstracts International $g 85-01.
790 $a 0183
791 $a M.Sc.
792 $a 2023
793 $a English
856 4 0 $u https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540024