Intergranular stress corrosion cracking and selective internal oxidation of nickel-chromium-iron alloys in hydrogenated steam.

Record Type:	Electronic resources : Monograph/item
Title/Author:	Intergranular stress corrosion cracking and selective internal oxidation of nickel-chromium-iron alloys in hydrogenated steam./
Author:	Capell, Brent M.
Description:	370 p.
Notes:	Source: Dissertation Abstracts International, Volume: 66-02, Section: B, page: 1146.
Contained By:	Dissertation Abstracts International66-02B.
Subject:	Engineering, Nuclear. -
Online resource:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3163761
ISBN:	0496980378

Intergranular stress corrosion cracking and selective internal oxidation of nickel-chromium-iron alloys in hydrogenated steam.
Capell, Brent M.

Intergranular stress corrosion cracking and selective internal oxidation of nickel-chromium-iron alloys in hydrogenated steam. - 370 p.

Source: Dissertation Abstracts International, Volume: 66-02, Section: B, page: 1146.

Thesis (Ph.D.)--University of Michigan, 2005.

Selective internal oxidation (SIO) is a mechanism of grain boundary embrittlement through the formation of intergranular oxides of Cr2O3. SIO is proposed as a mechanism to explain intergranular stress corrosion cracking (IGSCC) of Ni-base alloys in pressurized water reactor environments. The purpose of this work is to investigate SIO through a series of experiments using controlled-purity alloys in a controlled, low-pressure steam environment in which the oxygen potential is varied. Five alloys; Ni-9Fe, Ni-5Cr, LCr (Ni-5Cr-9Fe), CD85 (Ni-16Cr-9Fe) and HCr (Ni-30Cr-9Fe), were used in corrosion coupon exposure tests and constant extension rate tensile (CERT) tests at 550°C and 400°C in an environment consisting of a controlled mixture of hydrogen, water vapor and argon. The hydrogen-to-water vapor partial pressure ratio (PPR) was varied between 0.001 and 0.9 to control the oxygen partial pressure.

ISBN: 0496980378Subjects--Topical Terms:

1043651
Engineering, Nuclear.

Intergranular stress corrosion cracking and selective internal oxidation of nickel-chromium-iron alloys in hydrogenated steam.
LDR:03293nmm 2200289 4500 001 1846220
005 20051117110105.5
008 130614s2005 eng d
020 $a 0496980378
035 $a (UnM)AAI3163761
035 $a AAI3163761
040 $a UnM $c UnM
100 1 $a Capell, Brent M. $3 1934344
245 1 0 $a Intergranular stress corrosion cracking and selective internal oxidation of nickel-chromium-iron alloys in hydrogenated steam.
300 $a 370 p.
500 $a Source: Dissertation Abstracts International, Volume: 66-02, Section: B, page: 1146.
500 $a Chair: Gary S. Was.
502 $a Thesis (Ph.D.)--University of Michigan, 2005.
520 $a Selective internal oxidation (SIO) is a mechanism of grain boundary embrittlement through the formation of intergranular oxides of Cr2O3. SIO is proposed as a mechanism to explain intergranular stress corrosion cracking (IGSCC) of Ni-base alloys in pressurized water reactor environments. The purpose of this work is to investigate SIO through a series of experiments using controlled-purity alloys in a controlled, low-pressure steam environment in which the oxygen potential is varied. Five alloys; Ni-9Fe, Ni-5Cr, LCr (Ni-5Cr-9Fe), CD85 (Ni-16Cr-9Fe) and HCr (Ni-30Cr-9Fe), were used in corrosion coupon exposure tests and constant extension rate tensile (CERT) tests at 550°C and 400°C in an environment consisting of a controlled mixture of hydrogen, water vapor and argon. The hydrogen-to-water vapor partial pressure ratio (PPR) was varied between 0.001 and 0.9 to control the oxygen partial pressure.
520 $a The Ni-9Fe, Ni-5Cr and LCr alloys formed a uniform Ni(OH)2 film at PPR values less than 0.09 while CD85 and HCr formed Cr2O 3 oxide films over the entire PPR range. Corrosion coupon results also show the formation of highly localized oxide particles at grain boundaries. Focused ion beam analysis revealed that intergranular oxides were observed at significant depths (>150 nm) down grain boundaries and the oxide morphology depended on the alloy composition and PPR value. Diffusion of oxygen along the grain boundary accounted for the growth of intergranular oxides.
520 $a CERT test results showed that intergranular cracking was caused by creep-induced microvoid coalescence only at 550°C and did not depend on PPR. At 400°C, the cracking behavior depended on the PPR and resulted in a mixture of creep-induced microvoid coalescence and brittle intergranular failure. The cracked boundary fraction was higher at a PPR value where a Ni(OH)2 surface film formed. Alloy composition influenced cracking and the cracked boundary fraction decreased as the alloy chromium content increased. The compositions of oxides at intergranular crack tips were similar to intergranular oxides in corrosion coupons and demonstrated a link between intergranular oxide formation and intergranular cracking. The observation of intergranular oxides as well as the influence of alloy content on IG cracking was found to support SIO as a mechanism for IGSCC.
590 $a School code: 0127.
650 4 $a Engineering, Nuclear. $3 1043651
690 $a 0552
710 2 0 $a University of Michigan. $3 777416
773 0 $t Dissertation Abstracts International $g 66-02B.
790 1 0 $a Was, Gary S., $e advisor
790 $a 0127
791 $a Ph.D.
792 $a 2005
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3163761